产品物性表
 特性 |
|---|
| 熔融指数 |
| 成型收缩率 |
| 拉伸强度 |
| 断裂伸长率 |
| 弯曲强度 |
| 弯曲模量 |
| 悬臂梁缺口冲击 |
| 热变形温度 |
| 维卡软化点温度 |
| 阻燃性能 |
| 表面电阻率 |
| 体积电阻率 |
| 密度 |
测试标准 |
|---|
| ASTM D1238 |
| ASTM D955 |
| ASTM D638 |
| ASTM D638 |
| ASTM D790 |
| ASTM D790 |
| ASTM D256 |
| ASTM D648 |
| ASTMD1525 |
| UL 94 |
| IEC 60093 |
| IEC 60093 |
| ASTM D792 |
测试条件 |
|---|
|
260℃2.16kg 260℃5kg |
| 3.2mm |
| 50mm/min |
| 50mm/min |
| 2mm/min |
| 2mm/min |
|
3.2mm 23℃ 3.2mm -30℃ |
| 1.82Mpa |
| 50N 120℃/h |
| 1.6mm |
| - |
| - |
| 23℃ |
单位 |
|---|
|
g/10min g/10min |
| % |
| Mpa |
| % |
| Mpa |
| Mpa |
| J/m |
| ℃ |
| ℃ |
| Class |
| Ω |
| Ωom |
| kg/m3 |
A6110 |
|---|
|
6 18 |
| 0.5-0.7 |
| 58 |
| 80 |
| 80 |
| 2300 |
|
650 450 |
| 110 |
| 135 |
| HB |
| 1.00E+16 |
| 1.00E+14 |
| 1190 |
|
A6120 |
|---|
|
10 30 |
| 0.5-0.7 |
| 56 |
| 80 |
| 80 |
| 2300 |
|
640 440 |
| 107 |
| 130 |
| HB |
| 1.00E+16 |
| 1.00E+14 |
| 1150 |
|
A6130 |
|---|
|
10 31 |
| 0.5-0.7 |
| 56 |
| 80 |
| 80 |
| 2300 |
|
680 430 |
| 102 |
| 122 |
| HB |
| 1.00E+16 |
| 1.00E+14 |
| 1130 |
|
A6140 |
|---|
|
9.9 32 |
| 0.5-0.7 |
| 55 |
| 80 |
| 80 |
| 2300 |
|
608 420 |
| 99 |
| 118 |
| HB |
| 1.00E+16 |
| 1.00E+14 |
| 1124 |
|
A6150 |
|---|
|
10.2 34 |
| 0.5-0.7 |
| 53 |
| 80 |
| 80 |
| 2300 |
|
530 420 |
| 92 |
| 110 |
| HB |
| 1.00E+16 |
| 1.00E+14 |
| 1117 |
- ●上述数据是用注塑样品在23℃，湿度50%的条件下测得，数据为实验典型值，不作正式质保承诺。
- ●颜色产品的数据可能略有变化
塑料加工工艺
| 加工工艺 |
|---|
| A6110 |
| A6120 |
| A6130 |
| A6140 |
| A6150 |
- ●以上工艺参数仅供参考，具体要根据产品、注塑机和模具进行适当调整。